If you look closely at the base of the nose ring, you can see a even line or meniscus on both sides of the ring, where the glaze ends. This is an absolute indication that the lure was not sprayed, but dipped in to the glaze finish. If it had been sprayed, the end portion of the ring would have been masked off, in which case there would be a sharp and uneven parting line (without a meniscus) of the finish on the ring, when removing the masking tape.

The glaze into which the lure was dipped, had to be very thin and free flowing to allow such even coating all over the lure. I have watched Graphite USA (GUSA) coat their rod blanks by suspending them by the tip, then pouring a proprietary rod finish coating on the tip and allowing it to flow down covering the entire rod blank with a thin uniform coating. GUSA also puts color pigments into this coating to get the many beautiful colored rods that they produce.

Trondak's U-40 Perma Gloss, is the most likely glaze/coating on the lure. It is water thin and rapidly drys to a hard shell finish. Test the surface with you finger nail and if the finish is hard, then it's Perma Gloss. If it is relatively soft, then it is a much thinned rod wrapping epoxy.

Neptune

*

Link to comment
Share on other sites

Join the conversation

You can post now and register later. If you have an account, sign in now to post with your account.
Note: Your post will require moderator approval before it will be visible.

Guest
Reply to this topic...

×   Pasted as rich text.   Paste as plain text instead

  Only 75 emoji are allowed.

×   Your link has been automatically embedded.   Display as a link instead

×   Your previous content has been restored.   Clear editor

×   You cannot paste images directly. Upload or insert images from URL.

Loading...


×
×
  • Create New...
Top